| Metals : |
| Material description |
ASTM Specification |
Grades |
| Low-carbon austenitic stainless steel (carbon equal to or less than 0.03%) |
A 351/A 351M |
CF-3,CF-3A, |
| |
CF-3M,CF-3MA, |
| A 743/A 743M |
CF-3,CF-3M, |
| |
CF-3MN,CN-3M, |
| A 744/A 744M |
CF-3,CF-3M |
| Low-alloy steel (quenched and tempered) |
A 148/A 148M |
105-85,115-95, |
| |
135-125,150-135, |
| |
160-145,165-150, |
| |
165-150L,210-180, |
| |
210-180L, |
| |
260-210,260-210L |
| A 352/A 352M |
LC2-1,LC1,LC2, |
| |
LC3,LC4,LC9, |
| A 732/A 732M |
7Q,8Q,9Q,10Q,11Q, |
| |
12Q,13Q,14Q. |
| Carbon Steel (carbon less than 0.35% tensile strength less than or equal to 70 ksi (480 Mpa)) |
A 27/A 27M |
All Grades |
| A 216/A 216M |
WCA,WCB |
| A 352/A 352M |
LCB,LCA |
| A 356/A 356M |
1 |
| A 732/A 732M |
1A,2A |
| Low-alloy steel (annealed,normalised or normalised and tempered. Tensile strength less than 85 ksi (585 Mpa)) |
A 148/A 148M |
80-50 |
| A 217/A 217M |
WC1,WC4,WC5,WC6, |
| |
WC9 |
| A 352/A 352M |
LC1,LC2LC3,LC4 |
| A 356/A 356M |
2,5,6,8 |
| A 389/A 389M |
C23,C24 |
| Carbon steel (tensile strength greater than 70 ksi (480 Mpa)). Carbon-manganese steel (tensile strength equal to or greater than 70 ksi but less than 90 ksi (620 Mpa)) |
A 148/A 148M |
80-40 |
| A 216/A 216M |
WCC |
| A 352/A 352M |
LCC |
| A 732/A 732M |
2Q,3A |
| A 757/A 757M |
A2Q |
| Carbon and carbon-manganese steel (tensile strength equal to or greater than 90 ksi (620 Mpa)) |
A 732/A 732M |
3Q,4A,4Q,5N |
| Low-alloy steel (annealed, normalised or normalised and tempered. Tensile strength equal to or greater than 85ksi (585 Mpa)). |
A 148/A 148M |
90-60,105-85 |
| A 217/A 217M |
C5,C12,WC11 |
| A 356/A 356M |
9,10 |
| Ferritic Stainless steel |
A 743/A 743M |
CB-30,CC-50 |
| Martensitic Stainless steel |
A 217/A 217M |
CA-15 |
| A 352/A 352M |
CA6NM |
| A 356/A 356M |
CA6NM |
| A 487/A 487M |
CA15-A,CA15-B, |
| |
CA15-C,CA15-D, |
| |
CA15M-A,CA6NM-A, |
| |
CA6NM-B |
| A 743/A 743M |
CA-15,CA-15M, |
| |
CA6NM,CA-40, |
| |
CA6N |
| Unstabilised austenitic Stainless Steel (Carbon greater than 0.03%) |
A 351/A 351M |
CF-8,CF-8A, |
| |
CF-8M,CF-10, |
| |
CF-10M,CG-8M, |
| |
CH-8,CH-10, |
| |
CH-20 |
| A 447/A 447M |
Type 1 |
| A 743/A 743M |
CF-8,CG-12, |
| |
CF-20,CF-8M, |
| |
CF-16F,CH-20, |
| |
CG-8M,CE-30 |
| A 744/A 744M |
CF-8,CF-8M |
| |
CG-8M |
| Stabilised austenitic stainless steel |
A 351/A 351M |
CF-8C,CF-10MC, |
| |
CK-20,HK-30 |
| |
HK-40,HT-30, |
| |
CN-7M,CT-15C |
| A 447/A 447M |
Type II |
| A 743/A 743M |
CF-8C,CN-7M, |
| |
CN-7MS,CK-20 |
| A 744/A 744M |
CF-8C,CN-7M, |
| |
CN-7MS |
| Austenitic-ferritic stainless steel |
A 351/A 351M |
CD-4MCU |
| A 743/A 743M |
CD-4MCU |
| A 744/A 744M |
CD-4MCU |
| Precipitation-hardened austenitic stainless steel |
A 747/A 747M |
CB7CU-1,CB7CU-2 |
| Nickel-base alloys |
A 494/A 494M |
CW-12MW,CY-40, |
| CZ-100,M-35-1, |
| M-35-2,M-30C, |
| N-12MV,N-7M, |
| CW-6M,CW-6MC, |
| CW-2M,CX-2MW |
|